Study of Fracture Resistance of Nanolaminate Coatings Using Indentation and Impact Tests

• Autoři: BURŠÍKOVÁ Vilma; SOBOTA Jaroslav; GROSSMAN Jan; FOŘT Tomáš; DUPÁK Libor; ZÁBRANSKÝ Lukáš; SOUČEK Pavel; VAŠINA Petr; BURŠÍK Jiří
• Rok publikování: 2017
• Druh: Článek ve sborníku
• Konference: Material Structure & Micromechanics of Fracture VIII
• Fakulta / Pracoviště MU: Přírodovědecká fakulta
• Obor: Fyzika plazmatu a výboje v plynech
• Klíčová slova: impact test; fracture resistance; nanoindentation; differential hardness
• Popis: The aim of the present work was to study the mechanical properties of thin nanocomposite Mo-B-C coatings consisting of nanocrystalline Mo2BC embedded in amorphous Mo-B-C matrix. Magnetron sputtering of three targets, B4C, C and Mo, was used for coatings preparation. The Mo-B-C coatings were deposited on high speed steel substrates. The fracture resistance of Mo-B-C coatings was studied by both indentation and dynamic impact tests. The impact tests enabled us to predict the load limit causing the coating destruction.