Influence of substitution of Cr by Cu on phase equilibria and microstructures in the Fe-Ni-Co-Cr high-entropy alloys

Autoři

ZADERA Antonin SOPOUŠEK Jiří BURSIK Jiri CUPERA Jan BROŽ Pavel JAN Vit

Rok publikování 2024
Druh Článek v odborném periodiku
Časopis / Zdroj Intermetallics
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
www https://www.sciencedirect.com/science/article/abs/pii/S0966979524002747?via%3Dihub
Doi http://dx.doi.org/10.1016/j.intermet.2024.108455
Klíčová slova High-entropy alloys; Phase separation; Spinodal decomposition; Phase equilibria; CALPHAD
Přiložené soubory
Popis The article describes how substitution of chromium by copper affects phase equilibria in Fe-Ni-Co-Cr highentropy alloy. The alloys with copper content ranging from 0 to 20 % (at.) of Cu were prepared. The alloys were equilibrated at 900, 800, 700, and 650 C-degrees. The samples were investigated by electron microscopy, EDX spectroscopy, and EBSD method. The face-centred cubic phases have only occurred in equilibrated alloys: austenite matrix, copper-rich FCC(Cu) phase, and regions containing these phases. The compositions of equilibrated samples at annealing temperatures are given. Fine microstructures including a semicoherent FCC phase rich in Cu and an FCC phase including the main magnetic elements (Fe, Co, Ni) were formed. The experimental results were compared with the calculated phase equilibria obtained by the CALPHAD method.