Phase analysis of Creep-Resistant Fe-C-Cr-Mo-V(W) Steels after Long-Term Service Exposure

• Autoři: FORET Rudolf; SOPOUŠEK Jiří; KRUMPOS Josef; SVOBODA Milan; SOPOUŠEK Jiří; VŘEŠŤÁL Jan; SVOBODA Milan; VŘEŠŤÁL Jan
• Rok publikování: 2001
• Druh: Článek v odborném periodiku
• Časopis / Zdroj: Zeitschrift fur Metallkunde
• Fakulta / Pracoviště MU: Přírodovědecká fakulta
• Obor: Fyzikální chemie a teoretická chemie
• Klíčová slova: Creep-resistant steels; Phase analysis; Long-term service exposure
• Popis: "Industrial" samples of three low-alloy CrMoVW steel types exposed to long term use in power plants (30,900-141,500 h at temperatures of 500-510 C) were analysed using analytical electron microscopy. The carbides M7C3, M2C, MC, V4C3 and M23C6 were found in the body-centered cubic matrix. It was ascertained that, even after a very long service time, the samples were not entirely in a state of equilibrium. The difference between experimental and calculated results is briefly discussed.

Související projekty

• Kinetika precipitace karbidů v Cr-Mo ocelích
• Fázové rovnováhy v soustavách na bázi přechodových kovů s dusíkem a uhlíkem